Substrate Temperature Dependence of Film Thickness for Zm1-xCoxO (x=0.03 mol) Film by Rapid Oxalate Decomposition Technique

Author: Myint Myint Win1, Ohnmar Than2, Myint Kalayar3, Than Than Win4,Yin Maung Maung1 and Ko Ko Kyaw Soe1
Abstract:
       Co(0.3 mol) –doped Zinc oxide precursor was obtained by precipitation of the mixture of zinc-acetate, Co-acetate and oxalic acid. The Zn1-x CoxO gel  was poured with constant  rate (0.75 rpm) on the dependence of film thickness was systematically observed.

Key Words: zinc-acetate, Zm1-xCoxO gel, film thickness

Published:  Published:  Myanmar Academy of Arts and Science Research Journal (Vol.VII,No-2(A), March  2009, Physics)

Posted by at

1 comment:

  1. AnonymousFebruary 12, 2017 at 7:16 AM

    Hi admin,
    I read your blog,I really like it.which is abouot film thickness.
    The card is now properly positioned to guide the film thickness rolls into the rollers.
    Carefully monitor the threading card to ensure the leading edge is properly taken into the laminating machine.
    film thickness



    Thanks,

    jahaingiralam

    ReplyDelete

Subscribe to: Post Comments (Atom)